POLYPROPYLENE HOMOPOLYMER
Sasol Chemicals’ Polypropylene (PP) stands as a highly versatile thermoplastic, boasting an extensive range of applications across various industries. The POLYPROPYLENE HOMOPOLYMER product line, offered by Sasol, is extensively utilized in both injection moulding and extrusion conversion industries, underlining its broad adaptability and efficiency.
| Products | MFR (g/10min) | Tensile modulus (MPa) | Charpy notched impact strength @23°C kJ/m² | Conversion Techniques |
|---|---|---|---|---|
| HHR102 | 2 | 1650 | 4 | Blow moulding, Extrusion tapes and fibres (monofilament), Injection moulding, Thermoforming |
| HKR102 | 3.5 | 1600 | 3.5 | Extrusion tapes and fibres (monofilament), Injection moulding |
| HLR102 | 5.3 | 1550 | 3.5 | Extrusion tapes and fibres (monofilament), Injection moulding |
| HMR040 | 8.5 | 2000 | 3 | Injection moulding |
| HMR127 | 8.5 | 1550 | 3 | Extrusion film, Injection moulding |
| HNR100 | 12 | 1550 | 2.8 | Injection moulding |
| HNR101 | 12 | 1550 | 2.8 | Extrusion tapes and fibres (monofilament)\ |
| HRV140 | 20 | 1600 | 3 | Injection moulding |
| HSV103 | 30 | 1400 | 2.5 | Extrusion coating, Extrusion tapes and fibres (monofilament), Non-woven spunbound |
| HTV145 | 50 | 1650 | 2.5 | Extrusion coating, Injection moulding |
Products
HHR102
MFR (g/10min)
2
Tensile modulus (MPa)
1650
Charpy notched impact strength @23°C kJ/m²
4
Conversion Techniques
Blow moulding, Extrusion tapes and fibres (monofilament), Injection moulding, Thermoforming
Products
HKR102
MFR (g/10min)
3.5
Tensile modulus (MPa)
1600
Charpy notched impact strength @23°C kJ/m²
3.5
Conversion Techniques
Extrusion tapes and fibres (monofilament), Injection moulding
Products
HLR102
MFR (g/10min)
5.3
Tensile modulus (MPa)
1550
Charpy notched impact strength @23°C kJ/m²
3.5
Conversion Techniques
Extrusion tapes and fibres (monofilament), Injection moulding
Products
HMR040
MFR (g/10min)
8.5
Tensile modulus (MPa)
2000
Charpy notched impact strength @23°C kJ/m²
3
Conversion Techniques
Injection moulding
Products
HMR127
MFR (g/10min)
8.5
Tensile modulus (MPa)
1550
Charpy notched impact strength @23°C kJ/m²
3
Conversion Techniques
Extrusion film, Injection moulding
Products
HNR100
MFR (g/10min)
12
Tensile modulus (MPa)
1550
Charpy notched impact strength @23°C kJ/m²
2.8
Conversion Techniques
Injection moulding
Products
HNR101
MFR (g/10min)
12
Tensile modulus (MPa)
1550
Charpy notched impact strength @23°C kJ/m²
2.8
Conversion Techniques
Extrusion tapes and fibres (monofilament)\
Products
HRV140
MFR (g/10min)
20
Tensile modulus (MPa)
1600
Charpy notched impact strength @23°C kJ/m²
3
Conversion Techniques
Injection moulding
Products
HSV103
MFR (g/10min)
30
Tensile modulus (MPa)
1400
Charpy notched impact strength @23°C kJ/m²
2.5
Conversion Techniques
Extrusion coating, Extrusion tapes and fibres (monofilament), Non-woven spunbound
Products
HTV145
MFR (g/10min)
50
Tensile modulus (MPa)
1650
Charpy notched impact strength @23°C kJ/m²
2.5
Conversion Techniques
Extrusion coating, Injection moulding
| Product | File Type | Date Uploaded | |
|---|---|---|---|
| HHR102 SDS | 10 Jan 2024 | ||
| HKQ205 SDS | 10 Jan 2024 | ||
| HKR102 SDS | 10 Jan 2024 | ||
| HLR102 SDS | 10 Jan 2024 | ||
| HMR040 SDS | 10 Jan 2024 | ||
| HMR127 SDS | 10 Jan 2024 | ||
| HNR100 SDS | 10 Jan 2024 | ||
| HNR101 SDS | 10 Jan 2024 | ||
| HRV140 SDS | 10 Jan 2024 | ||
| HSV103 SDS | 10 Jan 2024 | ||
| HTV145 SDS | 10 Jan 2024 |
| Product | File Type | Date Uploaded | |
|---|---|---|---|
| HHR102 TDS | 10 Jan 2024 | ||
| HKQ205 TDS | 10 Jan 2024 | ||
| HKR102 TDS | 10 Jan 2024 | ||
| HLR102 TDS | 10 Jan 2024 | ||
| HMR040 TDS | 10 Jan 2024 | ||
| HMR127 TDS | 10 Jan 2024 | ||
| HNR100 TDS | 10 Jan 2024 | ||
| HNR101 TDS | 10 Jan 2024 | ||
| HRV140 TDS | 10 Jan 2024 | ||
| HSV103 TDS | 10 Jan 2024 | ||
| HTV145 TDS | 10 Jan 2024 |